In this stud y, we have investigated the possibility of improving the Voe, FF and 1J values of Cu20 solar cells while preserving the resulted high Jsc values. Here we report that controlling the growth of p-Cu20 by ...

Thin films of n-type cuprous oxide (Cu2O) were potentiostatically electrodeposited on a Ti substrate in an acetate bath. Cu2O thin films were annealed at 500 �C for 30 min in air for growing p-type cupric oxide (CuO) thin ...

Cross sections have been measured up to 35 MeV excitation for the 76Se(n,p)76As reaction at five laboratory angles between 0� and 15�. The incident neutron energy was 198 MeV. The distribution of Gamow-Teller (GT) strength ...

Copper Indium Disulphide thin films were grown by electrodeposition of Cu-ln alloy followed by sulphurisation in H2S gas. It was observed that the ionic concentration of Cu2+/ In3+ in the electrodepositing bath determines ...

CuInSe2 thin films were prepared on Ti plates by electrodeposition from an aqueous solution containing CuCl2, InCl3 and SeO2. The deposition was carried out at -0.5V Vs SCE. X-ray diffraction and Scanning electron microscopy ...

Measurements of the self-diffusion coefficient of water in NAFION-117 as a function of pressure have been carried out. The natural field gradient of a 7.3 T superconducting magnet was used for the diffusion measurement. ...